Pambuka
Baja tahan karat dikenal minangka baja paduan dhuwur.Dheweke kalebu 4-30% kromium.Padha diklasifikasikaké dadi martensitic, austenitic, lan baja ferritic adhedhasar struktur kristal.
Baja tahan karat kelas 317 minangka versi modifikasi saka baja tahan karat 316.Wis kekuatan dhuwur lan resistance karat.Lembar data ing ngisor iki menehi katrangan luwih lengkap babagan baja tahan karat kelas 317.
Komposisi kimia
Baja Tahan Karat – Grade 317 (UNS S31700)
Komposisi kimia baja tahan karat kelas 317 diterangake ing tabel ing ngisor iki.
| unsur | Isi (%) |
|---|---|
| Besi, Fe | 61 |
| Kromium, Kr | 19 |
| Nikel, Ni | 13 |
| Molibdenum, Mo | 3.50 |
| Mangan, Mn | 2 |
| Silikon, Si | 1 |
| Karbon, C | 0.080 |
| Fosfor, P | 0.045 |
| Sulfur, S | 0.030 |
Sifat Fisik
Baja Tahan Karat – Grade 317 (UNS S31700)
Tabel ing ngisor iki nuduhake sifat fisik baja tahan karat kelas 317.
| Properti | Metrik | Imperial |
|---|---|---|
| Kapadhetan | 8 g/cm3 | 0,289 lb/in³ |
| Titik lebur | 1370°C | 2550°F |
Sifat Mekanik
Baja Tahan Karat – Grade 317 (UNS S31700)
Sifat mekanik baja tahan karat 317 kelas anil ditampilake ing tabel ing ngisor iki.
| Properti | Metrik | Imperial |
|---|---|---|
| Kekuwatan tensile | 620 MPa | 89900 psi |
| kekuatan ngasilaken | 275 MPa | 39900 psi |
| Modulus elastis | 193 GPa | 27993 ksi |
| rasio Poisson | 0.27-0.30 | 0.27-0.30 |
| Elongation ing break (ing 50 mm) | 45% | 45% |
| Hardness, Rockwell B | 85 | 85 |
Sifat termal
Sifat termal baja tahan karat kelas 317 diwenehi ing tabel ing ngisor iki.
| Properti | Metrik | Imperial |
|---|---|---|
| Koefisien ekspansi termal (@ 0-100°C/32-212°F) | 16 µm/m°C | 8,89 µin/in°F |
| Konduktivitas termal (@ 100°C/212°F) | 16,3 W/mK | 113 BTU ing/jam.ft².°F |
Jeneng Liyane
Sebutan liyane sing padha karo baja tahan karat kelas 317 kalebu ing tabel ing ngisor iki.
| ASTM A167 | ASTM A276 | ASTM A478 | ASTM A814 | ASME SA403 |
| ASTM A182 | ASTM A312 | ASTM A511 | QQ S763 | ASME SA409 |
| ASTM A213 | ASTM A314 | ASTM A554 | DIN 1.4449 | MIL-S-862 |
| ASTM A240 | ASTM A403 | ASTM A580 | ASME SA 240 | SAE 30317 |
| ASTM A249 | ASTM A409 | ASTM A632 | ASME SA249 | SAE J405 (30317) |
| ASTM A269 | ASTM A473 | ASTM A813 | ASME SA 312 |
Fabrikasi lan Perawatan Panas
Kemampuan mesin
Nggolek peralatan kanggo nganalisa logam sampeyan?
Baja tahan karat kelas 317 luwih angel tinimbang baja tahan karat 304.Disaranake nggunakake pemutus chip.Hardenability saka alloy iki bakal suda yen feed pancet lan kacepetan kurang digunakake.
Welding
Baja tahan karat kelas 317 bisa dilas nggunakake metode fusi lan resistensi.Cara welding oxyacetylene ora disenengi kanggo campuran iki.AWS E / ER317 utawa 317L logam pangisi bisa digunakake kanggo entuk asil sing apik.
Panas Kerja
Baja tahan karat kelas 317 bisa digarap panas nggunakake kabeh prosedur kerja panas sing umum.Iki digawe panas ing 1149-1260 ° C (2100-2300 ° F).Sampeyan kudu ora digawe panas ing ngisor 927 ° C (1700 ° F).Anil post-work bisa ditindakake kanggo njaga sifat tahan korosi.
Kerja Dingin
Stamping, shearing, drawing, lan heading bisa ditindakake kanthi sukses.Anil pasca kerja ditindakake kanggo nyuda stres internal.