316L / S31603 stainless steel 7,0 * 0,3 mm kanggo penukar panas
Properti kasebut ditemtokake kanggo produk sing digulung rata (piring, lembaran, lan kumparan) ing ASTM A240 / A240M.Properti sing padha nanging ora kudu padha ditemtokake kanggo produk liyane kayata pipa lan bar ing spesifikasi masing-masing.
Komposisi
316L / S31603 stainless steel 7,0 * 0,3 mm kanggo penukar panas
Tabel 1.Range komposisi kanggo stainless steel 316L.
| sasmita | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
|---|---|---|---|---|---|---|---|---|---|---|
| 316L | Min | - | - | - | - | - | 16.0 | 2.00 | 10.0 | - |
| Maks | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 |
Sifat Mekanik
316L / S31603 stainless steel 7,0 * 0,3 mm kanggo penukar panas
Tabel 2.Sifat mekanik baja tahan karat 316L.
| sasmita | Tarik Str (MPa) min | Ngasilake Str 0,2% Bukti (MPa) min | Elong (% ing 50 mm) min | Kekerasan | |
|---|---|---|---|---|---|
| Rockwell B (HR B) maks | Brinell (HB) maks | ||||
| 316L | 485 | 170 | 40 | 95 | 217 |
Sifat Fisik
316L / S31603 stainless steel 7,0 * 0,3 mm kanggo penukar panas
Tabel 3.Sifat fisik khas kanggo baja tahan karat 316-grade.
| sasmita | Kapadhetan (kg/m3) | Modulus Elastik (GPa) | Rata-rata Co-eff Ekspansi Termal (µm/m/°C) | Konduktivitas termal (W/mK) | Kalor Spesifik 0-100 °C (J/kg.K) | Resistivitas listrik (nΩ.m) | |||
|---|---|---|---|---|---|---|---|---|---|
| 0-100 °C | 0-315 °C | 0-538 °C | Ing suhu 100 °C | Ing 500 ° C | |||||
| 316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Perbandingan Spesifikasi Grade
316L / S31603 stainless steel 7,0 * 0,3 mm kanggo penukar panas
Tabel 4.Spesifikasi kelas baja tahan karat 316L.
| sasmita | UNS No | Inggris lawas | Euronorm | SS Swedia | JIS Jepang | ||
|---|---|---|---|---|---|---|---|
| BS | En | No | jeneng | ||||
| 316L | S31603 | 316S11 | - | 1.4404 | X2CrNiMo17-12-2 | 2348 | SUS 316L |